Titanium Ti64 is a pre-alloyed TiAlV4 alloy in fine powder form. This well-known light alloy has excellent mechanical properties and corrosion resistance combined with low specific weight and biocompatibility. This material is ideal for many high-performance engineering applications, for example in aerospace and motor racing, and also for the production of biomedical implants.
- Direct manufacture of functional prototypes, small series products, individualized products or spare parts
- Parts requiring a combination of high mechanical properties and low specific weight, e.g., structural and engine components for aerospace and motor racing applications, etc.
- Biomedical implants
|Aluminum (Al) = 5.50 – 6.75%||Nitrogen (N) = max 0.05%||Iron (Fe) = max 0.30%|
|Vanadium (V) = 3.50 – 4.50%||Carbon (C) = max 0.08%||Other elements = max 0.40%|
|Oxygen (O) = max 0.20%||Hydrogen (H) = max 0.015%||Titanium (Ti) = Balance|
Stress relieve at 1200°F +/- 25°F for 3 hours +/- 15 minutes in a vacuum
Heat Treatment (HT):
(OPTION 1) 915°F for 6 hours (strength and hardness)
(OPTION 2) 1100°F for 6 hours (ductility)
Hot Isostatic Pressing (HIP):
|3DMT MATERIAL DATA|
|ASTM F1472 - Wrought for
(HIP and HT)
|0.02% Yield (ksi)||119.6 min||120 – 126 min||160||152.6||125.9|
|Ultimate Tensile (ksi)||129.8 min||130 – 135 min||170||164.1||140.9|
|Elongation (%)||6 – 10 min||6 – 10 min||15||11.5||10.9|
The data above is general information that may vary from machine to machine and supplier to supplier.